Polymer, resist composition and patterning process

ABSTRACT

A polymer comprising recurring units of formulae (1) and (2) wherein R 1  and R 3  are H or methyl, R 2  and R 4  are C 1-15  alkyl, R 5  to R 8  are H, or R 5  and R 7 , and R 6  and R 8  form trimethylene or 1,3-cyclopentylene and having a Mw of 1,000-500,000 is novel. A resist composition comprising the polymer as a base resin is sensitive to high-energy radiation, has excellent sensitivity, resolution and etching resistance and lends itself to micropatterning with electron beams or deep-UV.

This invention relates to (i) a polymer comprising specific recurring units, (ii) a resist composition comprising the polymer as a base resin, and (iii) a patterning process using the resist composition.

BACKGROUND OF THE INVENTION

While a number of recent efforts are being made to achieve a finer pattern rule in the drive for higher integration and operating speeds in LSI devices, deep-ultraviolet lithography is thought to hold particular promise as the next generation in microfabrication technology. In particular, photolithography using a KrF or ArF excimer laser as the light source is strongly desired to reach the practical level as the micropatterning technique capable of achieving a feature size of 0.3 μm or less.

For resist materials for use with KrF excimer lasers, polyhydroxystyrene having a practical level of transparency and etching resistance is, in fact, a standard base resin. For resist materials for use with ArF excimer lasers, polyacrylic or polymethacrylic acid derivatives containing an adamantane structure in their side chain are often used as described in JP-A 9-73173 and JP-A 9-90637. Few of these polymers are regarded as exhibiting satisfactory performance.

More particularly, resist compositions using derivatives of polyacrylic or polymethacrylic acid as the base resin exhibit satisfactory sensitivity and resolution upon pattern formation by exposure and development, but have extremely low dry etching resistance. It is possible to improve the dry etching resistance to some extent by introducing many acid-decomposable units having an adamantane structure as typified by 2-alkyl-2-adamantyl groups to increase the carbon density. The introduction of adamantane-containing acid-decomposable units, however, sacrifices resolving power and working convenience owing to their dull reactivity and is thus undesirable. Specifically, such polymers can give rise to many problems including a T-top profile of pattern, serration on pattern side-walls, deposition of foreign matter on the substrate and pattern, and substantial changes of sensitivity with minute shifts of heat treatment temperature. They are thus practically unacceptable. While a finer pattern rule is being demanded, there is a need to have a resist material which exerts satisfactory performance with respect to sensitivity and resolution, has practically acceptable etching resistance, and is convenient to work with due to a wide margin allowed for processing conditions.

SUMMARY OF THE INVENTION

Therefore, an object of the present invention is to provide (i) a polymer having a high resolution, practically acceptable etching resistance, and a substantial margin allowed for heat treatment temperature, (ii) a resist composition comprising the polymer as a base resin, and (iii) a patterning process using the resist composition.

It has been found that novel polymers comprising recurring units of the following general formulae (1) and (2) and having a weight average molecular weight of 1,000 to 500,000, which are produced by the method to be described later, have improved properties as the resist base resin; that a resist composition comprising the polymer as the base resin has a high resolution and practically acceptable etching resistance, and is convenient to work with due to a wide margin allowed for heat treatment temperature; and that this resist composition lends itself to precise micropatterning.

In a first aspect, the invention provides a polymer comprising recurring units of the general formula (1) and recurring units of the general formula (2) and having a weight average molecular weight of 1,000 to 500,000.

Herein R¹ and R³ each are hydrogen or methyl, R² and R⁴ each are a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, R⁵, R⁶, R⁷ and R⁸ each are hydrogen, or a pair of R⁵ and R⁷ and a pair of R⁶ and R⁸ each stand for a group of atoms to form trimethylene or 1,3-cyclopentylene.

The polymer may further include recurring units of the general formula (3).

Herein R⁹ is hydrogen or methyl, R¹⁰ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, R¹¹ is hydrogen or CO₂R¹², R¹² is a straight, branched or cyclic alkyl group having 1 to 15 carbon atoms in which at least one oxygen atom may intervene in any carbon-to-carbon bond, and X is methylene or an oxygen atom.

In a second aspect, the invention provides a resist composition comprising the inventive polymer as a base resin.

In a third aspect, the invention provides a process for forming a resist pattern comprising the steps of applying the resist composition onto a substrate to form a coating; heat treating the coating and then exposing it to high-energy radiation or electron beam through a photo mask; and optionally heat treating the exposed coating and developing it with a developer.

As described in the preamble, acid-decomposable units containing an adamantane structure have dull reactivity and adversely affect resolving power and ease of use, despite many advantages including excellent etching resistance and alleviated line density dependence. Based on the presumption that a satisfactory resist material is obtained by enhancing the acid decomposition reactivity of a polymer as a whole while keeping the advantages of adamantane-containing acid-decomposable units, we attempted to use recurring units containing an adamantane structure of formula (1) in combination with recurring units of formula (2) featuring a high acid decomposition reactivity and found that the object is achieved thereby. The recurring units of formula (3) are capable of imparting substrate adhesion, developer affinity and solvent solubility to the base resin, while minimizing any decline of etching resistance associated with the polar structure introduced, and therefore, better results are obtained by using the recurring units of formula (3) in combination with the units of formulae (1) and (2). Therefore, a resist composition using as a base resin the polymer comprising recurring units of formula (1), recurring units of formula (2) and optionally, recurring units of formula (3) according to the invention satisfies the performance factors of sensitivity and resolution, has practically acceptable dry etching resistance, is improved in substrate adhesion, developer affinity and solvent solubility, allows for a wide margin to the heat treatment temperature range, is convenient to use, and is thus very useful in forming micropatterns.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Polymer

Novel polymers or high molecular weight compounds according to the invention are defined as comprising recurring units of the following general formula (1) and recurring units of the following general formula (2). The polymers have a weight average molecular weight of 1,000 to 500,000.

Herein R¹ and R³ are hydrogen or methyl. R² and R⁴ are straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms, such as, for example, methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl, and butyladamantyl. R⁵, R⁶, R⁷ and R⁸ are hydrogen, or a pair of R⁵ and R⁷ and a pair of R⁶ and R⁸ each stand for a group of atoms to form trimethylene or 1,3-cyclopentylene.

The preferred polymers further include recurring units of the general formula (3).

Herein R⁹ is hydrogen or methyl. R¹⁰ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, examples of which are as enumerated above for R² and R⁴. R¹¹ is hydrogen or CO₂R¹² wherein R¹² is a straight, branched or cyclic alkyl group having 1 to 15 carbon atoms or a similar alkyl group in which one or more oxygen atoms intervene in any carbon-to-carbon bond. Suitable alkyl groups are as enumerated above for R² and R⁴, and examples of the alkyl group in which one or more oxygen atoms intervene in any carbon-to-carbon bond include methoxymethyl, methoxyethoxymethyl, 1-ethoxyethyl and 2-tetrahydropyranyl. X is methylene or an oxygen atom.

Illustrative, non-limiting examples of the recurring units of formula (1) are given below.

Illustrative, non-limiting examples of the recurring units of formula (2) are given below.

Illustrative, non-limiting examples of the recurring units of formula (3) are given below.

If desired, the polymers of the invention may further contain recurring units of one or more types selected from units of the following general formulae (M1) to (M9).

Herein, R⁰⁰¹ is hydrogen, methyl or CH₂CO₂R⁰⁰³. R⁰⁰² is hydrogen, methyl or CO₂R⁰⁰³. R⁰⁰³ is a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. R⁰⁰⁴ is hydrogen or a monovalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group. At least one of R⁰⁰⁵ to R⁰⁰⁸ represents a monovalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group while the remaining R's independently represent hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. Alternatively, R⁰⁰⁵ to R⁰⁰⁸, taken together, may form a ring, and in that event, at least one of R⁰⁰⁵ to R⁰⁰⁸ is a divalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. R⁰⁰⁹ is a monovalent hydrocarbon group of 2 to 15 carbon atoms having at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide. At least one of R⁰¹⁰ to R⁰¹³ is a monovalent hydrocarbon group of 2 to 15 carbon atoms having at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide, while the remaining R's are independently hydrogen or straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms. R⁰¹⁰ to R⁰¹³, taken together, may form a ring, and in that event, at least one of R⁰¹⁰ to R⁰¹³ is a divalent hydrocarbon group of 1 to 15 carbon atoms having at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. R⁰¹⁴ is a polycyclic hydrocarbon group having 7 to 15 carbon atoms or an alkyl group containing a polycyclic hydrocarbon group. R⁰¹⁵ is an acid labile group. X is CH₂ or an oxygen atom. Y is —O— or —(NR⁰¹⁶)— wherein R⁰¹⁶ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. Letter k is equal to 0 or 1.

More illustratively, R⁰⁰¹ is hydrogen, methyl or CH₂CO₂R⁰⁰³. R⁰⁰² is hydrogen, methyl or CO₂R⁰⁰³. R⁰⁰³ is a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, for example, methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl, and butyladamantyl.

R⁰⁰⁴ is hydrogen or a monovalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group, for example, hydrogen, carboxyethyl, carboxybutyl, carboxycyclopentyl, carboxycyclohexyl, carboxynorbornyl, carboxyadamantyl, hydroxyethyl, hydroxybutyl, hydroxycyclopentyl, hydroxycyclohexyl, hydroxynorbornyl, and hydroxyadamantyl.

At least one of R⁰⁰⁵ to R⁰⁰⁸ represents a monovalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group while the remaining R's independently represent hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. Examples of the carboxyl or hydroxyl-bearing monovalent hydrocarbon group of 1 to 15 carbon atoms include carboxy, carboxymethyl, carboxyethyl, carboxybutyl, hydroxymethyl, hydroxyethyl, hydroxybutyl, 2-carboxyethoxycarbonyl, 4-carboxybutoxycarbonyl, 2-hydroxyethoxycarbonyl, 4-hydroxybutoxycarbonyl, carboxycyclopentyloxycarbonyl, carboxycyclohexyloxycarbonyl, carboxynorbornyloxycarbonyl, carboxyadamantyloxycarbonyl, hydroxycyclopentyloxycarbonyl, hydroxycyclohexyloxycarbonyl, hydroxynorbornyloxycarbonyl, and hydroxyadamantyloxycarbonyl. Examples of the straight, branched or cyclic alkyl group of 1 to 15 carbon atoms are the same as exemplified for R⁰⁰³.

Alternatively, R⁰⁰⁵ to R⁰⁰⁸, taken together, may form a ring, and in that event, at least one of R⁰⁰⁵ to R⁰⁰⁸ is a divalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. Examples of the carboxyl or hydroxyl-bearing divalent hydrocarbon group of 1 to 15 carbon atoms include the groups exemplified as the carboxyl or hydroxyl-bearing monovalent hydrocarbon group, with one hydrogen atom eliminated therefrom. Examples of the straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms include the groups exemplified for R⁰⁰³, with one hydrogen atom eliminated therefrom.

R⁰⁰⁹ is a monovalent hydrocarbon group of 2 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide, for example, methoxymethyl, methoxyethoxymethyl, 2-oxooxolan-3-yl, 2-oxooxolan-4-yl, 4,4-dimethyl-2-oxooxolan-3-yl, 4-methyl-2-oxooxan-4-yl, 2-oxo-1,3-dioxolan-4-ylmethyl, and 5-methyl-2-oxooxolan-5-yl.

At least one of R⁰¹⁰ to R⁰¹³ is a monovalent hydrocarbon group of 2 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide, while the remaining R's are independently hydrogen or straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms. Examples of the monovalent hydrocarbon group of 2 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide include methoxymethyl, methoxymethoxymethyl, formyl, methylcarbonyl, formyloxy, acetoxy, pivaloyloxy, formyloxymethyl, acetoxymethyl, pivaloyloxymethyl, methoxycarbonyl, 2-oxooxolan-3-yloxycarbonyl, 4,4-dimethyl-2-oxooxolan-3-yloxycarbonyl, 4-methyl-2-oxooxan-4-yloxycarbonyl, 2-oxo-1,3-dioxolan-4-ylmethyloxycarbonyl, and 5-methyl-2-oxooxolan-5-yloxycarbonyl. Examples of the straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms are the same as exemplified for R⁰⁰³.

R⁰¹⁰ to R⁰¹³, taken together, may form a ring, and in that event, at least one of R⁰¹⁰ to R⁰¹³ is a divalent hydrocarbon group of 1 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. Examples of the divalent hydrocarbon group of 1 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide include 2-oxapropane-1,3-diyl, 1,1-dimethyl-2-oxapropane-1,3-diyl, 1-oxo-2-oxapropane-1,3-diyl, 1,3-dioxo-2-oxapropane-1,3-diyl, 1-oxo-2-oxabutane-1,4-diyl, and 1,3-dioxo-2-oxabutane-1,4-diyl, as well as the groups exemplified as the monovalent hydrocarbon group of 1 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide, with one hydrogen atom eliminated therefrom. Examples of the straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms include the groups exemplified for R⁰⁰³, with one hydrogen atom eliminated therefrom.

R⁰¹⁴ is a polycyclic hydrocarbon group having 7 to 15 carbon atoms or an alkyl group containing a polycyclic hydrocarbon group, for example, norbornyl, bicyclo[3.3.1]nonyl, tricyclo[5.2.1.0^(2,6)]decyl, adamantyl, ethyladamantyl, butyladamantyl, norbornylmethyl, and adamantylmethyl.

R⁰¹⁵ is an acid labile group, which will be described later. X is CH₂ or an oxygen atom. Y is —O— or —(NR⁰¹⁶)— wherein R⁰¹⁶ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, such as, for example, methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, cyclohexyl, ethylcyclopentyl, butylcyclopentyl, ethylcyclohexyl, butylcyclohexyl, adamantyl, ethyladamantyl and butyladamantyl. Letter k is equal to 0 or 1.

The acid labile groups represented by R⁰¹⁵ may be selected from a variety of such groups. Examples of the acid labile group are groups of the following general formulae (L1) to (L4), tertiary alkyl groups of 4 to 20 carbon atoms, preferably 4 to 15 carbon atoms, trialkylsilyl groups in which each alkyl moiety has 1 to 6 carbon atoms, and oxoalkyl groups of 4 to 20 carbon atoms.

In these formulae and throughout the specification, the broken line denotes a free valence bond. R^(L01) and R^(L02) are hydrogen or straight, branched or cyclic alkyl groups of 1 to 18 carbon atoms, preferably 1 to 10 carbon atoms. Exemplary alkyl groups include methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, cyclopentyl, cyclohexyl, 2-ethylhexyl, and n-octyl. R^(L03) is a monovalent hydrocarbon group of 1 to 18 carbon atoms, preferably 1 to 10 carbon atoms, which may contain a hetero atom such as oxygen, examples of which include unsubstituted straight, branched or cyclic alkyl groups and straight, branched or cyclic alkyl groups in which some hydrogen atoms are replaced by hydroxyl, alkoxy, oxo, amino, alkylamino or the like. Illustrative examples are the substituted alkyl groups shown below.

A pair of R^(L01) and R^(L02), R^(L01) and R^(L03), or R^(L02) and R^(L03) may form a ring. Each of R^(L01), R^(L02) and R^(L03) is a straight or branched alkylene group of 1 to 18 carbon atoms, preferably 1 to 10 carbon atoms when they form a ring.

R^(L04) is a tertiary alkyl group of 4 to 20 carbon atoms, preferably 4 to 15 carbon atoms, a trialkylsilyl group in which each alkyl moiety has 1 to 6 carbon atoms, an oxoalkyl group of 4 to 20 carbon atoms, or a group of formula (L1). Exemplary tertiary alkyl groups are tert-butyl, tert-amyl, 1,1-diethylpropyl, 2-cyclopentylpropan-2-yl, 2-cyclohexylpropan-2-yl, 2-(bicyclo[2.2.1]heptan-2-yl)propan-2-yl, 2-(adamantan-1-yl)propan-2-yl, 1-ethylcyclopentyl, 1-butylcyclopentyl, 1-ethylcyclohexyl, 1-butylcyclohexyl, 1-ethyl-2-cyclopentenyl, 1-ethyl-2-cyclohexenyl, 2-methyl-2-adamantyl, and 2-ethyl-2-adamantyl. Exemplary trialkylsilyl groups are trimethylsilyl, triethylsilyl, and dimethyl-tert-butylsilyl. Exemplary oxoalkyl groups are 3-oxocyclohexyl, 4-methyl-2-oxooxan-4-yl, and 5-methyl-2-oxooxolan-5-yl. Letter y is an integer of 0 to 6.

R^(L05) is a monovalent hydrocarbon group of 1 to 8 carbon atoms which may contain a hetero atom or a substituted or unsubstituted aryl group of 6 to 20 carbon atoms. Examples of the monovalent hydrocarbon group which may contain a hetero atom include straight, branched or cyclic alkyl groups such as methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, cyclopentyl, and cyclohexyl, and substituted groups in which some hydrogen atoms on the foregoing groups are substituted with hydroxyl, alkoxy, carboxy, alkoxycarbonyl, oxo, amino, alkylamino, cyano, mercapto, alkylthio, sulfo or other groups. Exemplary aryl groups are phenyl, methylphenyl, naphthyl, anthryl, phenanthryl, and pyrenyl. Letter m is equal to 0 or 1, n is equal to 0, 1, 2 or 3, and 2m+n is equal to 2 or 3.

R^(L06) is a monovalent hydrocarbon group of 1 to 8 carbon atoms which may contain a hetero atom or a substituted or unsubstituted aryl group of 6 to 20 carbon atoms. Examples of these groups are the same as exemplified for R^(L05).

R^(L07) to R^(L16) independently represent hydrogen or monovalent hydrocarbon groups of 1 to 15 carbon atoms which may contain a hetero atom. Exemplary hydrocarbon groups are straight, branched or cyclic alkyl groups such as methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, tert-amyl, n-pentyl, n-hexyl, n-octyl, n-nonyl, n-decyl, cyclopentyl, cyclohexyl, cyclopentylmethyl, cyclopentylethyl, cyclopentylbutyl, cyclohexylmethyl, cyclohexylethyl and cyclohexylbutyl, and substituted ones of these groups in which some hydrogen atoms are replaced by hydroxyl, alkoxy, carboxy, alkoxycarbonyl, oxo, amino, alkylamino, cyano, mercapto, alkylthio, sulfo or other groups. Alternatively, R^(L07) to R^(L16), taken together, form a ring (for example, a pair of R^(L07) and R^(L08), R^(L07) and R^(L09), R^(L08) and R^(L10), R^(L09) and R^(L10), R^(L11) and R^(L12), R^(L13) and R^(L14), or a similar pair form a ring). Each of R^(L07) to R^(L16) represents a divalent C₁-C₁₅ hydrocarbon group which may contain a hetero atom, when they form a ring, examples of which are the ones exemplified above for the monovalent hydrocarbon groups, with one hydrogen atom being eliminated. Two of R^(L07) to R^(L16) which are attached to adjoining carbon atoms (for example, a pair of R^(L07) and R^(L09), R^(L09) and R^(L15), R^(L13) and R^(L15), or a similar pair) may bond together directly to form a double bond.

Of the acid labile groups of formula (L1), the straight and branched ones are exemplified by the following groups.

Of the acid labile groups of formula (L1), the cyclic ones are, for example, tetrahydrofuran-2-yl, 2-methyltetrahydrofuran-2-yl, tetrahydropyran-2-yl, and 2-methyltetrahydropyran-2-yl.

Examples of the acid labile groups of formula (L2) include tert-butoxycarbonyl, tert-butoxycarbonylmethyl, tert-amyloxycarbonyl, tert-amyloxycarbonylmethyl, 1,1-diethylpropyloxycarbonyl, 1,1-diethylpropyloxycarbonylmethyl, 1-ethylcyclopentyloxycarbonyl, 1-ethylcyclopentyloxycarbonylmethyl, 1-ethyl-2-cyclopentenyloxycarbonyl, 1-ethyl-2-cyclopentenyloxycarbonylmethyl, 1-ethoxyethoxy-carbonylmethyl, 2-tetrahydropyranyloxycarbonylmethyl, and 2-tetrahydrofuranyloxycarbonylmethyl groups.

Examples of the acid labile groups of formula (L3) include 1-methylcyclopentyl, 1-ethylcyclopentyl, 1-n-propylcyclopentyl, 1-isopropylcyclopentyl, 1-n-butylcyclopentyl, 1-sec-butylcyclopentyl, 1-cyclohexylcyclopentyl, 1-(4-methoxy-n-butyl)cyclopentyl, 1-methylcyclohexyl, 1-ethylcyclohexyl, 3-methyl-1-cyclopenten-3-yl, 3-ethyl-1-cyclopenten-3-yl, 3-methyl-1-cyclohexen-3-yl, and 3-ethyl-1-cyclohexen-3-yl groups.

The acid labile groups of formula (L4) are exemplified by the following groups.

Examples of the tertiary alkyl groups of 4 to 20 carbon atoms, trialkylsilyl groups in which each alkyl moiety has 1 to 6 carbon atoms, and oxoalkyl groups of 4 to 20 carbon atoms are as exemplified for R^(L04).

The recurring units of formulae (M1) to (M9) are effective for imparting such desired properties as developer affinity, substrate adhesion and etching resistance to a resist composition based on a polymer comprising these recurring units. By adjusting the content of these recurring units, the performance of the resist composition can be finely adjusted.

The polymers of the invention have a weight average molecular weight of about 1,000 to 500,000, preferably about 3,000 to 100,000, as measured by gel permeation chromatography (GPC) using a polystyrene standard. Outside the range, the etching resistance may become extremely low and the resolution may become low because a substantial difference in rate of dissolution before and after exposure is lost.

The polymer of the invention can be prepared through copolymerization reaction using compounds of the following general formulae (1a) and (2a) as first and second monomers, optionally a compound of the following general formula (3a) as a third monomer, and optionally one or more members selected from compounds of the following general formulae (M1a) to (M9a) as subsequent monomers.

Herein, R¹ to R¹¹ and X are as defined above.

Herein, k, R⁰⁰¹ to R⁰¹⁵, X, and Y are as defined above.

By properly adjusting the proportion of the respective monomers used in the copolymerization reaction, the polymer can be tailored so that it may exert the preferred performance when blended in resist compositions.

In addition to (i) the monomer of formula (1a) and the monomer of formula (2a), (ii) the monomer of formula (3a), and (iii) the monomer or monomers of formulae (M1a) to (M9a), the polymer of the invention may have copolymerized therewith (iv) another monomer having a carbon-to-carbon double bond other than (i) to (iii). Examples of the additional monomer (iv) include substituted acrylic acid esters such as methyl methacrylate, methyl crotonate, dimethyl maleate, and dimethyl itaconate, unsaturated carboxylic acids such as maleic acid, fumaric acid and itaconic acid, substituted or unsubstituted norbornenes such as norbornene and methyl norbornene-5-carboxylate, and unsaturated acid anhydrides such as itaconic anhydride.

In the polymers of the invention, the preferred proportion of recurring units based on the respective monomers is, but not limited to, in the following range:

(i) 1 to 90 mol %, preferably 5 to 80 mol %, and more preferably 10 to 70 mol % of recurring units of formula (1) based on the monomer of formula (1a),

(ii) 1 to 90 mol %, preferably 5 to 80 mol %, and more preferably 10 to 70 mol % of recurring units of formula (2) based on the monomer of formula (2a),

(iii) 0 to 90 mol %, preferably 5 to 80 mol %, and more preferably 10 to 70 mol % of recurring units of formula (3) based on the monomer of formula (3a),

(iv) 0 to 60 mol %, preferably 0 to 40 mol %, and more preferably 0 to 30 mol % of recurring units of formulae (M1) to (M9) based on the monomers of formulae (M1a) to (M9a), and

(v) 0 to 60 mol %, preferably 0 to 40 mol %, and more preferably 0 to 30 mol % of recurring units based on another monomer.

The monomer of formula (1a) from which the units of formula (1) included essentially in the inventive polymers originate may be selected from commercially available monomers or prepared by well-known organic chemistry processes using 2-adamantanone as the starting material. The monomer of formula (2a) from which the units of formula (2) originate can be prepared by the process described in JP-A 2000-336121. The monomer of formula (3a) from which the units of formula (3) originate can be prepared by the process described in JP-A 2000-159758.

A variety of copolymerization reaction methods may be used for the preparation of the polymer according to the invention. The preferred polymerization reaction is radical polymerization.

For radical polymerization, preferred reaction conditions include (a) a solvent selected from among hydrocarbons such as benzene, ethers such as tetrahydrofuran, alcohols such as ethanol, and ketones such as methyl isobutyl ketone, (b) a polymerization initiator selected from azo compounds such as 2,2′-azobisisobutyronitrile and peroxides such as benzoyl peroxide and lauroyl peroxide, (c) a temperature of about 0° C. to about 100° C., and (d) a time of about ½ hour to about 48 hours. Reaction conditions outside the described range may be employed if desired.

Resist Composition

Since the polymer of the invention is useful as the base resin of a resist composition, the other aspect of the invention provides a resist composition, especially a chemically amplified positive resist composition, comprising the polymer. Typically, the resist composition contains the polymer, a photoacid generator, and an organic solvent, and other optional components.

Photoacid Generator

The photoacid generator is a compound capable of generating an acid upon exposure to high energy radiation or electron beams and includes the following:

(i) onium salts of the formula (P1a-1), (P1a-2) or (P1b),

(ii) diazomethane derivatives of the formula (P2),

(iii) glyoxime derivatives of the formula (P3),

(iv) bissulfone derivatives of the formula (P4),

(v) sulfonic acid esters of N-hydroxyimide compounds of the formula (P5),

(vi) β-ketosulfonic acid derivatives,

(vii) disulfone derivatives,

(viii) nitrobenzylsulfonate derivatives, and

(ix) sulfonate derivatives.

These photoacid generators are described in detail.

(i) Onium Salts of Formula (P1a-1), (P1a-2) or (P1b):

Herein, R^(101a), R^(101b), and R^(101c) independently represent straight, branched or cyclic alkyl, alkenyl, oxoalkyl or oxoalkenyl groups of 1 to 12 carbon atoms, aryl groups of 6 to 20 carbon atoms, or aralkyl or aryloxoalkyl groups of 7 to 12 carbon atoms, wherein some or all of the hydrogen atoms may be replaced by alkoxy or other groups. Also, R¹⁰¹b and R^(101c), taken together, may form a ring. R^(101b) and R^(101c) each are alkylene groups of 1 to 6 carbon atoms when they form a ring. K⁻ is a non-nucleophilic counter ion.

R^(101a), R^(101b), and R^(101c) may be the same or different and are illustrated below. Exemplary alkyl groups include methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclopropylmethyl, 4-methylcyclo-hexyl, cyclohexylmethyl, norbornyl, and adamantyl. Exemplary alkenyl groups include vinyl, allyl, propenyl, butenyl, hexenyl, and cyclohexenyl. Exemplary oxoalkyl groups include 2-oxocyclopentyl and 2-oxocyclohexyl as well as 2-oxopropyl, 2-cyclopentyl-2-oxoethyl, 2-cyclohexyl-2-oxoethyl, and 2-(4-methylcyclohexyl)-2-oxoethyl. Exemplary aryl groups include phenyl and naphthyl; alkoxyphenyl groups such as p-methoxyphenyl, m-methoxyphenyl, o-methoxyphenyl, ethoxyphenyl, p-tert-butoxyphenyl, and m-tert-butoxyphenyl; alkylphenyl groups such as 2-methylphenyl, 3-methylphenyl, 4-methylphenyl, ethylphenyl, 4-tert-butylphenyl, 4-butylphenyl, and dimethylphenyl; alkylnaphthyl groups such as methylnaphthyl and ethylnaphthyl; alkoxynaphthyl groups such as methoxynaphthyl and ethoxynaphthyl; dialkylnaphthyl groups such as dimethylnaphthyl and diethylnaphthyl; and dialkoxynaphthyl groups such as dimethoxynaphthyl and diethoxynaphthyl. Exemplary aralkyl groups include benzyl, phenylethyl, and phenethyl. Exemplary aryloxoalkyl groups are 2-aryl-2-oxoethyl groups such as 2-phenyl-2-oxoethyl, 2-(1-naphthyl)-2-oxoethyl, and 2-(2-naphthyl)-2-oxoethyl. Examples of the non-nucleophilic counter ion represented by K⁻ include halide ions such as chloride and bromide ions, fluoroalkylsulfonate ions such as triflate, 1,1,1-trifluoroethanesulfonate, and nonafluorobutanesulfonate, arylsulfonate ions such as tosylate, benzenesulfonate, 4-fluorobenzenesulfonate, and 1,2,3,4,5-pentafluorobenzene-sulfonate, and alkylsulfonate ions such as mesylate and butanesulfonate.

Herein, R^(102a) and R^(102b) independently represent straight, branched or cyclic alkyl groups of 1 to 8 carbon atoms. R¹⁰³ represents a straight, branched or cyclic alkylene groups of 1 to 10 carbon atoms. R^(104a) and R^(104b) independently represent 2-oxoalkyl groups of 3 to 7 carbon atoms. K⁻ is a non-nucleophilic counter ion.

Illustrative of the groups represented by R^(102a) and R^(102b) are methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, cyclopentyl, cyclohexyl, cyclopropylmethyl, 4-methylcyclohexyl, and cyclohexylmethyl. Illustrative of the groups represented by R¹⁰³ are methylene, ethylene, propylene, butylene, pentylene, hexylene, heptylene, octylene, nonylene, 1,4-cyclohexylene, 1,2-cyclohexylene, 1,3-cyclopentylene, 1,4-cyclooctylene, and 1,4-cyclohexanedimethylene. Illustrative of the groups represented by R^(104a) and R^(104b) are 2-oxopropyl, 2-oxocyclo-pentyl, 2-oxocyclohexyl, and 2-oxocycloheptyl. Illustrative examples of the counter ion represented by K⁻ are the same as exemplified for formulae (P1a-1) and (P1a-2).

(ii) Diazomethane Derivatives of Formula (P2)

Herein, R¹⁰⁵ and R¹⁰⁶ independently represent straight, branched or cyclic alkyl or halogenated alkyl groups of 1 to 12 carbon atoms, aryl or halogenated aryl groups of 6 to 20 carbon atoms, or aralkyl groups of 7 to 12 carbon atoms.

Of the groups represented by R¹⁰⁵ and R¹⁰⁶, exemplary alkyl groups include methyl, ethyl, propyl, isopropyl, n-butyl, sec-butyl, tert-butyl, pentyl, hexyl, heptyl, octyl, amyl, cyclopentyl, cyclohexyl, cycloheptyl, norbornyl, and adamantyl. Exemplary halogenated alkyl groups include trifluoromethyl, 1,1,1-trifluoroethyl, 1,1,1-trichloroethyl, and nonafluorobutyl. Exemplary aryl groups include phenyl;

alkoxyphenyl groups such as p-methoxyphenyl, m-methoxyphenyl, o-methoxyphenyl, ethoxyphenyl, p-tert-butoxyphenyl, and m-tert-butoxyphenyl; and alkylphenyl groups such as 2-methylphenyl, 3-methylphenyl, 4-methylphenyl, ethylphenyl, 4-tert-butylphenyl, 4-butylphenyl, and dimethylphenyl. Exemplary halogenated aryl groups include fluorophenyl, chlorophenyl, and 1,2,3,4,5-pentafluorophenyl. Exemplary aralkyl groups include benzyl and phenethyl.

(iii) Glyoxime Derivatives of Formula (P3)

Herein, R¹⁰⁷, R¹⁰⁸, and R¹⁰⁹ independently represent straight, branched or cyclic alkyl or halogenated alkyl groups of 1 to 12 carbon atoms, aryl or halogenated aryl groups of 6 to 20 carbon atoms, or aralkyl groups of 7 to 12 carbon atoms. Also, R¹⁰⁸ and R¹⁰⁹, taken together, may form a ring. R¹⁰⁸ and R¹⁰⁹ each are straight or branched alkylene groups of 1 to 6 carbon atoms when they form a ring.

Illustrative examples of the alkyl, halogenated alkyl, aryl, halogenated aryl, and aralkyl groups represented by R¹⁰⁷, R¹⁰⁸, and R¹⁰⁹ are the same as exemplified for R¹⁰⁵ and R¹⁰⁶. Examples of the alkylene groups represented by R¹⁰⁸ and R¹⁰⁹ include methylene, ethylene, propylene, butylene, and hexylene.

(iv) Bissulfone Derivatives of Formula (P4)

Herein, R^(101a) and R^(101b) are as defined above. (v) Sulfonic acid esters of N-hydroxyimide compounds of formula (P5)

Herein, R¹¹⁰ is an arylene group of 6 to 10 carbon atoms, alkylene group of 1 to 6 carbon atoms, or alkenylene group of 2 to 6 carbon atoms wherein some or all of the hydrogen atoms may be replaced by straight or branched alkyl or alkoxy groups of 1 to 4 carbon atoms, nitro, acetyl, or phenyl groups. R¹¹¹ is a straight, branched or cyclic alkyl group of 1 to 8 carbon atoms, alkenyl, alkoxyalkyl, phenyl or naphthyl group wherein some or all of the hydrogen atoms may be replaced by alkyl or alkoxy groups of 1 to 4 carbon atoms, phenyl groups (which may have substituted thereon an alkyl or alkoxy of 1 to 4 carbon atoms, nitro, or acetyl group), hetero-aromatic groups of 3 to 5 carbon atoms, or chlorine or fluorine atoms.

Of the groups represented by R¹¹⁰, exemplary arylene groups include 1,2-phenylene and 1,8-naphthylene; exemplary alkylene groups include methylene, ethylene, trimethylene, tetramethylene, phenylethylene, and norbornene-2,3-diyl; and exemplary alkenylene groups include 1,2-vinylene, 1-phenyl-1,2-vinylene, and 5-norbornene-2,3-diyl. Of the groups represented by R¹¹¹, exemplary alkyl groups are as exemplified for R^(101a) to R^(101c); exemplary alkenyl groups include vinyl, 1-propenyl, allyl, 1-butenyl, 3-butenyl, isoprenyl, 1-pentenyl, 3-pentenyl, 4-pentenyl, dimethylallyl, 1-hexenyl, 3-hexenyl, 5-hexenyl, 1-heptenyl, 3-heptenyl, 6-heptenyl, and 7-octenyl; and exemplary alkoxyalkyl groups include methoxymethyl, ethoxymethyl, propoxymethyl, butoxymethyl, pentyloxymethyl, hexyloxymethyl, heptyloxy-methyl, methoxyethyl, ethoxyethyl, propoxyethyl, butoxyethyl, pentyloxyethyl, hexyloxyethyl, methoxypropyl, ethoxypropyl, propoxypropyl, butoxypropyl, methoxybutyl, ethoxybutyl, propoxybutyl, methoxypentyl, ethoxypentyl, methoxyhexyl, and methoxyheptyl.

Of the substituents on these groups, the alkyl groups of 1 to 4 carbon atoms include methyl, ethyl, propyl, isopropyl, n-butyl, isobutyl and tert-butyl; the alkoxy groups of 1 to 4 carbon atoms include methoxy, ethoxy, propoxy, isopropoxy, n-butoxy, isobutoxy, and tert-butoxy; the phenyl groups which may have substituted thereon an alkyl or alkoxy of 1 to 4 carbon atoms, nitro, or acetyl group include phenyl, tolyl, p-tert-butoxyphenyl, p-acetylphenyl and p-nitrophenyl; the hetero-aromatic groups of 3 to 5 carbon atoms include pyridyl and furyl.

Illustrative examples of the photoacid generator include:

onium salts such as diphenyliodonium trifluoromethanesulfonate, (p-tert-butoxyphenyl)phenyliodonium trifluoromethanesulfonate, diphenyliodonium p-toluenesulfonate, (p-tert-butoxyphenyl)phenyliodonium p-toluenesulfonate, triphenylsulfonium trifluoromethanesulfonate, (p-tert-butoxyphenyl)diphenylsulfonium trifluoromethanesulfonate, bis(p-tert-butoxyphenyl)phenylsulfonium trifluoromethanesulfonate, tris(p-tert-butoxyphenyl)sulfonium trifluoromethanesulfonate, triphenylsulfonium p-toluenesulfonate, (p-tert-butoxyphenyl)diphenylsulfonium p-toluenesulfonate, bis(p-tert-butoxyphenyl)phenylsulfonium p-toluenesulfonate, tris(p-tert-butoxyphenyl)sulfonium p-toluenesulfonate, triphenylsulfonium nonafluorobutanesulfonate, triphenylsulfonium butanesulfonate, trimethylsulfonium trifluoromethanesulfonate, trimethylsulfonium p-toluenesulfonate, cyclohexylmethyl(2-oxocyclohexyl)sulfonium trifluoromethanesulfonate, cyclohexylmethyl(2-oxocyclohexyl)sulfonium p-toluenesulfonate, dimethylphenylsulfonium trifluoromethanesulfonate, dimethylphenylsulfonium p-toluenesulfonate, dicyclohexylphenylsulfonium trifluoromethanesulfonate, dicyclohexylphenylsulfonium p-toluenesulfonate, trinaphthylsulfonium trifluoromethanesulfonate, cyclohexylmethyl(2-oxocyclohexyl)sulfonium trifluoromethanesulfonate, (2-norbornyl)methyl(2-oxocyclohexyl)sulfonium trifluoromethanesulfonate, ethylenebis[methyl(2-oxocyclopentyl)sulfonium trifluoromethanesulfonate], and 1,2′-naphthylcarbonylmethyltetrahydrothiophenium triflate;

diazomethane derivatives such as bis(benzenesulfonyl)diazomethane, bis(p-toluenesulfonyl)diazomethane, bis(xylenesulfonyl)diazomethane, bis(cyclohexylsulfonyl)diazomethane, bis(cyclopentylsulfonyl)diazomethane, bis(n-butylsulfonyl)diazomethane, bis(isobutylsulfonyl)diazomethane, bis(sec-butylsulfonyl)diazomethane, bis(n-propylsulfonyl)diazomethane, bis(isopropylsulfonyl)diazomethane, bis(tert-butylsulfonyl)diazomethane, bis(n-amylsulfonyl)diazomethane, bis(isoamylsulfonyl)diazomethane, bis(sec-amylsulfonyl)diazomethane, bis(tert-amylsulfonyl)diazomethane, 1-cyclohexylsulfonyl-1-(tert-butylsulfonyl)diazomethane, 1-cyclohexylsulfonyl-1-(tert-amylsulfonyl)diazomethane, and 1-tert-amylsulfonyl-1-(tert-butylsulfonyl)diazomethane;

glyoxime derivatives such as bis-O-(p-toluenesulfonyl)-α-dimethylglyoxime, bis-O-(p-toluenesulfonyl)-α-diphenylglyoxime, bis-O-(p-toluenesulfonyl)-α-dicyclohexylglyoxime, bis-O-(p-toluenesulfonyl)-2,3-pentanedioneglyoxime, bis-O-(p-toluenesulfonyl)-2-methyl-3,4-pentanedioneglyoxime, bis-O-(n-butanesulfonyl)-α-dimethylglyoxime, bis-O-(n-butanesulfonyl)-α-diphenylglyoxime, bis-O-(n-butanesulfonyl)-α-dicyclohexylglyoxime, bis-O-(n-butanesulfonyl)2,3-pentanedioneglyoxime, bis-O-(n-butanesulfonyl)-2-methyl-3,4-pentanedioneglyoxime, bis-O-(methanesulfonyl)-α-dimethylglyoxime, bis-O-(trifluoromethanesulfonyl)-α-dimethylglyoxime, bis-O-(1,1,1-trifluoroethanesulfonyl)-α-dimethylglyoxime, bis-O-(tert-butanesulfonyl)-α-dimethylglyoxime, bis-O-(perfluorooctanesulfonyl)-α-dimethylglyoxime, bis-O-(cyclohexanesulfonyl)-α-dimethylglyoxime, bis-O-(benzenesulfonyl)-α-dimethylglyoxime, bis-O-(p-fluorobenzenesulfonyl)-α-dimethylglyoxime, bis-O-(p-tert-butylbenzenesulfonyl)-α-dimethylglyoxime, bis-O-(xylenesulfonyl)-α-dimethylglyoxime, and bis-O-(camphorsulfonyl)-α-dimethylglyoxime;

bissulfone derivatives such as bisnaphthylsulfonyl-methane, bistrifluoromethylsulfonylmethane, bismethyl-sulfonylmethane, bisethylsulfonylmethane, bispropylsulfonyl-methane, bisisopropylsulfonylmethane, bis-p-toluenesulfonyl-methane, and bisbenzenesulfonylmethane;

β-ketosulfone derivatives such as 2-cyclohexyl-carbonyl-2-(p-toluenesulfonyl)propane and 2-isopropyl-carbonyl-2-(p-toluenesulfonyl)propane;

disulfone derivatives such as diphenyl disulfone and dicyclohexyl disulfone;

nitrobenzyl sulfonate derivatives such as 2,6-dinitrobenzyl p-toluenesulfonate and 2,4-dinitrobenzyl p-toluenesulfonate;

sulfonic acid ester derivatives such as 1,2,3-tris(methanesulfonyloxy)benzene, 1,2,3-tris(trifluoro-methanesulfonyloxy)benzene, and 1,2,3-tris(p-toluene-sulfonyloxy)benzene; and

sulfonic acid esters of N-hydroxyimides such as N-hydroxysuccinimide methanesulfonate, N-hydroxysuccinimide trifluoromethanesulfonate, N-hydroxysuccinimide ethanesulfonate, N-hydroxysuccinimide 1-propanesulfonate, N-hydroxysuccinimide 2-propanesulfonate, N-hydroxysuccin-imide 1-pentanesulfonate, N-hydroxysuccinimide 1-octanesulfonate, N-hydroxysuccinimide p-toluenesulfonate, N-hydroxysuccinimide p-methoxybenzenesulfonate, N-hydroxy-succinimide 2-chloroethanesulfonate, N-hydroxysuccinimide benzenesulfonate, N-hydroxysuccinimide 2,4,6-trimethyl-benzenesulfonate, N-hydroxysuccinimide 1-naphthalene-sulfonate, N-hydroxysuccinimide 2-naphthalenesulfonate, N-hydroxy-2-phenylsuccinimide methanesulfonate, N-hydroxy-maleimide methanesulfonate, N-hydroxymaleimide ethane-sulfonate, N-hydroxy-2-phenylmaleimide methanesulfonate, N-hydroxyglutarimide methanesulfonate, N-hydroxyglutarimide benzenesulfonate, N-hydroxyphthalimide methanesulfonate, N-hydroxyphthalimide benzenesulfonate, N-hydroxyphthalimide trifluoromethanesulfonate, N-hydroxyphthalimide p-toluene-sulfonate, N-hydroxynaphthalimide methanesulfonate, N-hydroxynaphthalimide benzenesulfonate, N-hydroxy-5-norbornene-2,3-dicarboxyimide methanesulfonate, N-hydroxy-5-norbornene-2,3-dicarboxyimide trifluoromethanesulfonate, and N-hydroxy-5-norbornene-2,3-dicarboxyimide p-toluenesulfonate.

Preferred among these photoacid generators are onium salts such as triphenylsulfonium trifluoromethanesulfonate, (p-tert-butoxyphenyl)diphenylsulfonium trifluoromethane-sulfonate, tris(p-tert-butoxyphenyl)sulfonium trifluoro-methanesulfonate, triphenylsulfonium p-toluenesulfonate, (p-tert-butoxyphenyl)diphenylsulfonium p-toluenesulfonate, tris(p-tert-butoxyphenyl)sulfonium p-toluenesulfonate, trinaphthylsulfonium trifluoromethanesulfonate, cyclohexyl-methyl(2-oxocyclohexyl)sulfonium trifluoromethanesulfonate, (2-norbornyl)methyl(2-oxocylohexyl)sulfonium trifluoro-methanesulfonate, and 1,2′-naphthylcarbonylmethyltetrahydro-thiophenium triflate; diazomethane derivatives such as bis(benzenesulfonyl)diazomethane, bis(p-toluenesulfonyl)-diazomethane, bis(cyclohexylsulfonyl)diazomethane, bis(n-butylsulfonyl)diazomethane, bis(isobutylsulfonyl)-diazomethane, bis(sec-butylsulfonyl)diazomethane, bis(n-propylsulfonyl)diazomethane, bis(isopropylsulfonyl)-diazomethane, and bis(tert-butylsulfonyl)diazomethane; glyoxime derivatives such as bis-O-(p-toluenesulfonyl)-α-dimethylglyoxime and bis-O-(n-butanesulfonyl)-α-dimethylglyoxime; bissulfone derivatives such as bisnaphthylsulfonylmethane; and sulfonic acid esters of N-hydroxyimide compounds such as N-hydroxysuccinimide methanesulfonate, N-hydroxysuccinimide trifluoromethane-sulfonate, N-hydroxysuccinimide 1-propanesulfonate, N-hydroxysuccinimide 2-propanesulfonate, N-hydroxysuccin-imide 1-pentanesulfonate, N-hydroxysuccinimide p-toluene-sulfonate, N-hydroxynaphthalimide methanesulfonate, and N-hydroxynaphthalimide benzenesulfonate.

These photoacid generators may be used singly or in combinations of two or more thereof. Onium salts are effective for improving rectangularity, while diazomethane derivatives and glyoxime derivatives are effective for reducing standing waves. The combination of an onium salt with a diazomethane or a glyoxime derivative allows for fine adjustment of the profile.

The photoacid generator is preferably added in an amount of 0.1 to 15 parts, and especially 0.5 to 8 parts by weight, per 100 parts by weight of the base resin (all parts are by weight, hereinafter). Less than 0.1 part of the photoacid generator would provide a poor sensitivity whereas more than 15 parts of the photoacid generator would adversely affect transparency and resolution.

Organic Solvent

The organic solvent used herein may be any organic solvent in which the base resin, photoacid generator, and other components are soluble. Illustrative, non-limiting, examples of the organic solvent include ketones such as cyclohexanone and methyl-2-n-amylketone; alcohols such as 3-methoxybutanol, 3-methyl-3-methoxybutanol, 1-methoxy-2-propanol, and 1-ethoxy-2-propanol; ethers such as propylene glycol monomethyl ether, ethylene glycol monomethyl ether, propylene glycol monoethyl ether, ethylene glycol monoethyl ether, propylene glycol dimethyl ether, and diethylene glycol dimethyl ether; esters such as propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, ethyl lactate, ethyl pyruvate, butyl acetate, methyl 3-methoxypropionate, ethyl 3-ethoxypropionate, tert-butyl acetate, tert-butyl propionate, and propylene glycol mono-tert-butyl ether acetate; and lactones such as γ-butyrolactone. These solvents may be used alone or in combinations of two or more thereof. Of the above organic solvents, it is recommended to use diethylene glycol dimethyl ether and 1-ethoxy-2-propanol because the photoacid generator is most soluble therein, propylene glycol monomethyl ether acetate because it is a safe solvent, or a mixture thereof.

An appropriate amount of the organic solvent used is about 200 to 1,000 parts, especially about 400 to 800 parts by weight per 100 parts by weight of the base resin.

Other Polymer

To the resist composition of the invention, another polymer different from the inventive polymer may also be added. The other polymers that can be added to the resist composition are, for example, those polymers comprising units of the following formula (R1) and/or (R2) and having a weight average molecular weight of about 1,000 to about 500,000, especially about 5,000 to about 100,000 although the other polymers are not limited thereto.

Herein, R⁰⁰¹ is hydrogen, methyl or CH₂CO₂R⁰⁰³. R⁰⁰² is hydrogen, methyl or CO₂R⁰⁰³. R⁰⁰³ is a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. R⁰⁰⁴ is hydrogen or a monovalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group. At least one of R⁰⁰⁵ to R⁰⁰⁸ represents a monovalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group while the remaining R's independently represent hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms. Alternatively, R⁰⁰⁵ to R⁰⁰⁸, taken together, may form a ring, and in that event, at least one of R⁰⁰⁵ to R⁰⁰⁸ is a divalent hydrocarbon group of 1 to 15 carbon atoms having a carboxyl or hydroxyl group, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. R⁰⁰⁹ is a monovalent hydrocarbon group of 2 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide. At least one of R⁰¹⁰ to R⁰¹³ is a monovalent hydrocarbon group of 2 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide, while the remaining R's are independently hydrogen or straight, branched or cyclic alkyl groups of 1 to 15 carbon atoms. R⁰¹⁰ to R⁰¹³, taken together, may form a ring, and in that event, at least one of R⁰¹⁰ to R⁰¹³ is a divalent hydrocarbon group of 1 to 15 carbon atoms containing at least one partial structure selected from among ether, aldehyde, ketone, ester, carbonate, acid anhydride, amide and imide, while the remaining R's are independently single bonds or straight, branched or cyclic alkylene groups of 1 to 15 carbon atoms. R⁰¹⁴ is a polycyclic hydrocarbon group having 7 to 15 carbon atoms or an alkyl group containing a polycyclic hydrocarbon group. R⁰¹⁵ is an acid labile group. R⁰¹⁶ is hydrogen or methyl. R⁰¹⁷ is a straight, branched or cyclic alkyl group of 1 to 8 carbon atoms. X is CH₂ or an oxygen atom. Letter k′ is equal to 0 or 1; a1′, a2′, a3′, b1′, b2′, b3′, c1′, c2′, c3′, d1′, d2′, d3′, and e′ are numbers from 0 to less than 1, satisfying

a1′+a2′+a3′+b1′+b2′+b3′+c1′+c2′+c3′+d1′+d2′+d3′+e′=1; f′, g′, h′, i′, and j′ are numbers from 0 to less than 1, satisfying f′+g′+h′+i′+j′=1; x′, y′ and z′ each are an integer of 0 to 3, satisfying 1≦x′+y′+z′≦5 and 1≦y′+z′≦3.

Exemplary groups of these R's are as exemplified above.

The inventive polymer and the other polymer are preferably blended in a weight ratio from 100:0 to 10:90, more preferably from 100:0 to 20:80. If the blend ratio of the inventive polymer is below this range, the resist composition would become poor in some of the desired properties. The properties of the resist composition can be adjusted by properly changing the blend ratio of the inventive polymer.

The other polymer is not limited to one type and a mixture of two or more other polymers may be added. The use of plural polymers allows for easy adjustment of resist properties.

Dissolution Regulator

To the resist composition, a dissolution regulator may be added. The dissolution regulator is a compound having on the molecule at least two phenolic hydroxyl groups, in which an average of from 0 to 100 mol % of all the hydrogen atoms on the phenolic hydroxyl groups are replaced with acid labile groups or a compound having on the molecule at least one carboxyl group, in which an average of 50 to 100 mol % of all the hydrogen atoms on the carboxyl groups are replaced with acid labile groups, both the compounds having an average molecular weight within a range of 100 to 1,000, and preferably 150 to 800.

The degree of substitution of the hydrogen atoms on the phenolic hydroxyl groups with acid labile groups is on average at least 0 mol %, and preferably at least 30 mol %, of all the phenolic hydroxyl groups. The upper limit is 100 mol %, and preferably 80 mol %. The degree of substitution of the hydrogen atoms on the carboxyl groups with acid labile groups is on average at least 50 mol %, and preferably at least 70 mol %, of all the carboxyl groups, with the upper limit being 100 mol %.

Preferable examples of such compounds having two or more phenolic hydroxyl groups or compounds having at least one carboxyl group include those of formulas (D1) to (D14) below.

In these formulas, R²⁰¹ and R²⁰² are each hydrogen or a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms; R²⁰³ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or —(R²⁰⁷)_(h)—COOH; R²⁰⁴ is —(CH₂)₁— (where i=2 to 10), an arylene of 6 to 10 carbon atoms, carbonyl, sulfonyl, an oxygen atom, or a sulfur atom; R²⁰⁵ is an alkylene of 1 to 10 carbon atoms, an arylene of 6 to 10 carbon atoms, carbonyl, sulfonyl, an oxygen atom, or a sulfur atom; R²⁰⁶ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or a hydroxyl-substituted phenyl or naphthyl; R²⁰⁷ is a straight or branched alkylene of 1 to 10 carbon atoms; R²⁰⁸ is hydrogen or hydroxyl; the letter j is an integer from 0 to 5; u and h are each 0 or 1; s, t, s′, t′, s″, and t″ are each numbers which satisfy s+t=8, s′+t′=5, and s″+t″=4, and are such that each phenyl skeleton has at least one hydroxyl group; and α is a number such that the compounds of formula (D8) or (D9) have a molecular weight of from 100 to 1,000.

In the above formulas, suitable examples of R²⁰¹ and R²⁰² include hydrogen, methyl, ethyl, butyl, propyl, ethynyl, and cyclohexyl; suitable examples of R²⁰³ include the same groups as for R²⁰¹ and R²⁰², as well as —COOH and CH₂COOH; suitable examples of R²⁰⁴ include ethylene, phenylene, carbonyl, sulfonyl, oxygen, and sulfur; suitable examples of R²⁰⁵ include methylene as well as the same groups as for R²⁰⁴; and suitable examples of R²⁰⁶ include hydrogen, methyl, ethyl, butyl, propyl, ethynyl, cyclohexyl, and hydroxyl-substituted phenyl or naphthyl.

Exemplary acid labile groups on the dissolution regulator include groups of the following general formulae (L1) to (L4), tertiary alkyl groups of 4 to 20 carbon atoms, trialkylsilyl groups in which each of the alkyls has 1 to 6 carbon atoms, and oxoalkyl groups of 4 to 20 carbon atoms.

In these formulas, R^(L01) and R^(L02) are each hydrogen or a straight, branched or cyclic alkyl having 1 to 18 carbon atoms; and R^(L03) is a monovalent hydrocarbon group of 1 to 18 carbon atoms which may contain a heteroatom (e.g., oxygen). A pair of R^(L01) and R^(L02), a pair of R^(L01) and R^(L03), or a pair of R^(L02) and R^(L03) may together form a ring, with the proviso that R^(L01), R^(L02), and R^(L03) are each a straight or branched alkylene of 1 to 18 carbon atoms when they form a ring. R^(L04) is a tertiary alkyl group of 4 to 20 carbon atoms, a trialkysilyl group in which each of the alkyls has 1 to 6 carbon atoms, an oxoalkyl group of 4 to 20 carbon atoms, or a group of the formula (L1). R^(L05) is a monovalent hydrocarbon groups of 1 to 8 carbon atoms which may contain a hetero atom or a substituted or unsubstituted aryl group of 6 to 20 carbon atoms. R^(L06) is a monovalent hydrocarbon group of 1 to 8 carbon atoms which may contain a hetero atom or a substituted or unsubstituted aryl group of 6 to 20 carbon atoms. R^(L07) to R^(L16) independently represent hydrogen or monovalent hydrocarbon groups of 1 to 15 carbon atoms which may contain a hetero atom. Alternatively, R^(L07) to R^(L16), taken together, may form a ring. Each of R^(L07) to R^(L16) represents a divalent C₁-C₁₅ hydrocarbon group which may contain a hetero atom, when they form a ring. Two of R^(L07) to R^(L16) which are attached to adjoining carbon atoms may bond together directly to form a double bond. Letter y is an integer of 0 to 6. Letter m is equal to 0 or 1, n is equal to 0, 1, 2 or 3, and 2m+n is equal to 2 or 3. Illustrative examples of these groups are as previously exemplified.

The dissolution regulator may be formulated in an amount of 0 to 50 parts, preferably 0 to 40 parts, and more preferably 0 to 30 parts, per 100 parts of the base resin, and may be used singly or as a mixture of two or more thereof. The use of more than 50 parts would lead to slimming of the patterned film, and thus a decline in resolution.

The dissolution regulator can be synthesized by introducing acid labile groups into a compound having phenolic hydroxyl or carboxyl groups in accordance with an organic chemical formulation.

Basic Compound

In the resist composition of the invention, a basic compound may be blended. A suitable basic compound used herein is a compound capable of suppressing the rate of diffusion when the acid generated by the photoacid generator diffuses within the resist film. The inclusion of this type of basic compound holds down the rate of acid diffusion within the resist film, resulting in better resolution. In addition, it suppresses changes in sensitivity following exposure, thus reducing substrate and environment dependence, as well as improving the exposure latitude and the pattern profile.

Examples of basic compounds include primary, secondary, and tertiary aliphatic amines, mixed amines, aromatic amines, heterocyclic amines, carboxyl group-bearing nitrogenous compounds, sulfonyl group-bearing nitrogenous compounds, hydroxyl group-bearing nitrogenous compounds, hydroxyphenyl group-bearing nitrogenous compounds, alcoholic nitrogenous compounds, amide derivatives, and imide derivatives.

Examples of suitable primary aliphatic amines include ammonia, methylamine, ethylamine, n-propylamine, isopropylamine, n-butylamine, iso-butylamine, sec-butylamine, tert-butylamine, pentylamine, tert-amylamine, cyclopentyl amine, hexylamine, cyclohexylamine, heptylamine, octylamine, nonylamine, decylamine, dodecylamine, cetylamine, methylene-diamine, ethylenediamine, and tetraethylenepentamine. Examples of suitable secondary aliphatic amines include dimethylamine, diethylamine, di-n-propylamine, di-iso-propylamine, di-n-butylamine, di-iso-butylamine, di-sec-butylamine, dipentylamine, dicyclopentylamine, dihexylamine, dicyclohexylamine, diheptylamine, dioctylamine, dinonylamine, didecylamine, didodecylamine, dicetylamine, N,N-dimethylmethylenediamine, N,N-dimethylethylenediamine, and N,N-dimethyltetraethylenepentamine. Examples of suitable tertiary aliphatic amines include trimethylamine, triethylamine, tri-n-propylamine, tri-iso-propylamine, tri-n-butylamine, tri-iso-butylamine, tri-sec-butylamine, tripentylamine, tricyclopentylamine, trihexylamine, tricyclohexylamine, triheptylamine, trioctylamine, trinonylamine, tridecylamine, tridodecylamine, tricetylamine, N,N,N′,N′-tetramethylmethylenediamine, N,N,N′,N′-tetramethylethylenediamine, and N,N,N′,N′-tetramethyltetraethylenepentamine.

Examples of suitable mixed amines include dimethylethylamine, methylethylpropylamine, benzylamine, phenethylamine, and benzyldimethylamine. Examples of suitable aromatic and heterocyclic amines include aniline derivatives (e.g., aniline, N-methylaniline, N-ethylaniline, N-propylaniline, N,N-dimethylaniline, 2-methylaniline, 3-methylaniline, 4-methylaniline, ethylaniline, propylaniline, trimethylaniline, 2-nitroaniline, 3-nitroaniline, 4-nitroaniline, 2,4-dinitroaniline, 2,6-dinitroaniline, 3,5-dinitroaniline, and N,N-dimethyltoluidine), diphenyl(p-tolyl)amine, methyldiphenylamine, triphenylamine, phenylenediamine, naphthylamine, diamino-naphthalene, pyrrole derivatives (e.g., pyrrole, 2H-pyrrole, 1-methylpyrrole, 2,4-dimethylpyrrole, 2,5-dimethylpyrrole, and N-methylpyrrole), oxazole derivatives (e.g., oxazole and isooxazole), thiazole derivatives (e.g., thiazole and isothiazole), imidazole derivatives (e.g., imidazole, 4-methylimidazole, and 4-methyl-2-phenylimidazole), pyrazole derivatives, furazan derivatives, pyrroline derivatives (e.g., pyrroline and 2-methyl-1-pyrroline), pyrrolidine derivatives (e.g., pyrrolidine, N-methylpyrrolidine, pyrrolidinone, and N-methylpyrrolidone), imidazoline derivatives, imidazolidine derivatives, pyridine derivatives (e.g., pyridine, methylpyridine, ethylpyridine, propylpyridine, butylpyridine, 4-(1-butylpentyl)pyridine, dimethylpyridine, trimethylpyridine, triethylpyridine, phenylpyridine, 3-methyl-2-phenylpyridine, 4-tert-butylpyridine, diphenylpyridine, benzylpyridine, methoxypyridine, butoxypyridine, dimethoxypyridine, 1-methyl-2-pyridone, 4-pyrrolidinopyridine, 1-methyl-4-phenylpyridine, 2-(1-ethylpropyl)pyridine, aminopyridine, and dimethylaminopyridine), pyridazine derivatives, pyrimidine derivatives, pyrazine derivatives, pyrazoline derivatives, pyrazolidine derivatives, piperidine derivatives, piperazine derivatives, morpholine derivatives, indole derivatives, isoindole derivatives, 1H-indazole derivatives, indoline derivatives, quinoline derivatives (e.g., quinoline and 3-quinolinecarbonitrile), isoquinoline derivatives, cinnoline derivatives, quinazoline derivatives, quinoxaline derivatives, phthalazine derivatives, purine derivatives, pteridine derivatives, carbazole derivatives, phenanthridine derivatives, acridine derivatives, phenazine derivatives, 1,10-phenanthroline derivatives, adenine derivatives, adenosine derivatives, guanine derivatives, guanosine derivatives, uracil derivatives, and uridine derivatives.

Examples of suitable carboxyl group-bearing nitrogenous compounds include aminobenzoic acid, indolecarboxylic acid, and amino acid derivatives (e.g. nicotinic acid, alanine, alginine, aspartic acid, glutamic acid, glycine, histidine, isoleucine, glycylleucine, leucine, methionine, phenylalanine, threonine, lysine, 3-aminopyrazine-2-carboxylic acid, and methoxyalanine). Examples of suitable sulfonyl group-bearing nitrogenous compounds include 3-pyridinesulfonic acid and pyridinium p-toluenesulfonate. Examples of suitable hydroxyl group-bearing nitrogenous compounds, hydroxyphenyl group-bearing nitrogenous compounds, and alcoholic nitrogenous compounds include 2-hydroxypyridine, aminocresol, 2,4-quinolinediol, 3-indolemethanol hydrate, monoethanolamine, diethanolamine, triethanolamine, N-ethyldiethanolamine, N,N-diethylethanolamine, triisopropanolamine, 2,2′-iminodiethanol, 2-aminoethanol, 3-amino-1-propanol, 4-amino-1-butanol, 4-(2-hydroxyethyl)morpholine, 2-(2-hydroxyethyl)pyridine, 1-(2-hydroxyethyl)piperazine, 1-[2-(2-hydroxyethoxy)ethyl]-piperazine, piperidine ethanol, 1-(2-hydroxyethyl)pyrrolidine, 1-(2-hydroxyethyl)-2-pyrrolidinone, 3-piperidino-1,2-propanediol, 3-pyrrolidino-1,2-propanediol, 8-hydroxyjulolidine, 3-quinuclidinol, 3-tropanol, 1-methyl-2-pyrrolidine ethanol, 1-aziridine ethanol, N-(2-hydroxyethyl)phthalimide, and N-(2-hydroxyethyl)isonicotinamide. Examples of suitable amide derivatives include formamide, N-methylformamide, N,N-dimethylformamide, acetamide, N-methylacetamide, N,N-dimethylacetamide, propionamide, and benzamide. Suitable imide derivatives include phthalimide, succinimide, and maleimide.

In addition, basic compounds of the following general formula (B1) may also be included alone or in admixture.

N(X)_(n)(Y)_(3-n)  B1

In the formula, n is equal to 1, 2 or 3; Y is independently hydrogen or a straight, branched or cyclic alkyl group of 1 to 20 carbon atoms which may contain a hydroxyl group or ether; and X is independently selected from groups of the following general formulas (X1) to (X3), and two or three X's may bond together to form a ring.

In the formulas, R³⁰⁰, R³⁰² and R³⁰⁵ are independently straight or branched alkylene groups of 1 to 4 carbon atoms; R³⁰¹, R³⁰⁴ and R³⁰⁶ are independently hydrogen, straight, branched or cyclic alkyl groups of 1 to 20 carbon atoms, which may contain at least one hydroxyl group, ether group, ester group or lactone ring; and R³⁰³ is a single bond or a straight or branched alkylene group of 1 to 4 carbon atoms.

Illustrative examples of the compounds of formula (B1) include tris(2-methoxymethoxyethyl)amine, tris{2-(2-methoxyethoxy)ethyl}amine, tris{2-(2-methoxyethoxymethoxy)ethyl}amine, tris{2-(1-methoxyethoxy)ethyl}amine, tris{2-(1-ethoxyethoxy)ethyl}amine, tris{2-(1-ethoxypropoxy)ethyl}amine, tris[2-{2-(2-hydroxyethoxy)ethoxy}ethyl]amine, 4,7,13,16,21,24-hexaoxa-1,10-diazabicyclo[8.8.8]hexacosane, 4,7,13,18-tetraoxa-1,10-diazabicyclo[8.5.5]eicosane, 1,4,10,13-tetraoxa-7,16-diazabicyclooctadecane, 1-aza-12-crown-4, 1-aza-15-crown-5, 1-aza-18-crown-6, tris(2-formyloxyethyl)amine, tris(2-acetoxyethyl)amine, tris(2-propionyloxyethyl)amine, tris(2-butyryloxyethyl)amine, tris(2-isobutyryloxyethyl)amine, tris(2-valeryloxyethyl)amine, tris(2-pivaloyloxyethyl)amine, N,N-bis(2-acetoxyethyl)-2-(acetoxyacetoxy)ethylamine, tris(2-methoxycarbonyloxyethyl)amine, tris(2-tert-butoxycarbonyloxyethyl)amine, tris[2-(2-oxopropoxy)ethyl]amine, tris[2-(methoxycarbonylmethyl)oxyethyl]amine, tris[2-(tert-butoxycarbonylmethyloxy)ethyl]amine, tris[2-(cyclohexyloxycarbonylmethyloxy)ethyl]amine, tris(2-methoxycarbonylethyl)amine, tris(2-ethoxycarbonylethyl)amine, N,N-bis(2-hydroxyethyl)-2-(methoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(methoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-(ethoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(ethoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-(2-methoxyethoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(2-methoxyethoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-(2-hydroxyethoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(2-acetoxyethoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-[(methoxycarbonyl)methoxycarbonyl]ethylamine, N,N-bis(2-acetoxyethyl)-2-[(methoxycarbonyl)methoxycarbonyl]ethylamine, N,N-bis(2-hydroxyethyl)-2-(2-oxopropoxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(2-oxopropoxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-(tetrahydrofurfuryloxycarbonyl)ethylamine, N,N-bis(2-acetoxyethyl)-2-(tetrahydrofurfuryloxycarbonyl)ethylamine, N,N-bis(2-hydroxyethyl)-2-[(2-oxotetrahydrofuran-3-yl)oxycarbonyl]ethylamine, N,N-bis(2-acetoxyethyl)-2-[(2-oxotetrahydrofuran-3-yl)oxycarbonyl]ethylamine, N,N-bis(2-hydroxyethyl)-2-(4-hydroxybutoxycarbonyl)ethylamine, N,N-bis(2-formyloxyethyl)-2-(4-formyloxybutoxycarbonyl)ethylamine, N,N-bis(2-formyloxyethyl)-2-(2-formyloxyethoxycarbonyl)ethylamine, N,N-bis(2-methoxyethyl)-2-(methoxycarbonyl)ethylamine, N-(2-hydroxyethyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-(2-acetoxyethyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-(2-hydroxyethyl)-bis[2-(ethoxycarbonyl)ethyl]amine, N-(2-acetoxyethyl)-bis[2-(ethoxycarbonyl)ethyl]amine, N-(3-hydroxy-1-propyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-(3-acetoxy-1-propyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-(2-methoxyethyl)-bis[2-(methoxycarbonyl)ethyl]amine, N-butyl-bis[2-(methoxycarbonyl)ethyl]amine, N-butyl-bis[2-(2-methoxyethoxycarbonyl)ethyl]amine, N-methyl-bis(2-acetoxyethyl)amine, N-ethyl-bis(2-acetoxyethyl)amine, N-methyl-bis(2-pivaloyloxyethyl)amine, N-ethyl-bis[2-(methoxycarbonyloxy)ethyl]-amine, N-ethyl-bis[2-(tert-butoxycarbonyloxy)ethyl]amine, tris(methoxycarbonylmethyl)amine, tris(ethoxycarbonylmethyl)amine, N-butyl-bis(methoxycarbonylmethyl)amine, N-hexyl-bis(methoxycarbonylmethyl)amine, and β-(diethyl-amino)-δ-valerolactone.

Also useful are one or more of cyclic structure-bearing basic compounds having the following general formula (B2).

Herein X is as defined above, and R³⁰⁷ is a straight or branched alkylene group of 2 to 20 carbon atoms which may contain one or more carbonyl groups, ether structures, ester structures or sulfide structures.

Illustrative examples of the cyclic structure-bearing basic compounds having formula (B2) include 1-[2-(methoxymethoxy)ethyl]pyrrolidine, 1-[2-(methoxymethoxy)ethyl]piperidine, 4-[2-(methoxymethoxy)ethyl]morpholine, 1-[2-[(2-methoxyethoxy)methoxy]ethyl]pyrrolidine, 1-[2-[(2-methoxyethoxy)methoxy]ethyl]piperidine, 4-[2-[(2-methoxyethoxy)methoxy]ethyl]morpholine, 2-(1-pyrrolidinyl)ethyl acetate, 2-piperidinoethyl acetate, 2-morpholinoethyl acetate, 2-(1-pyrrolidinyl)ethyl formate, 2-piperidinoethyl propionate, 2-morpholinoethyl acetoxyacetate, 2-(1-pyrrolidinyl)ethyl methoxyacetate, 4-[2-(methoxycarbonyloxy)ethyl]morpholine, 1-[2-(t-butoxycarbonyloxy)ethyl]piperidine, 4-[2-(2-methoxyethoxycarbonyloxy)ethyl]morpholine, methyl 3-(1-pyrrolidinyl)propionate, methyl 3-piperidinopropionate, methyl 3-morpholinopropionate, methyl 3-(thiomorpholino)propionate, methyl 2-methyl-3-(1-pyrrolidinyl)propionate, ethyl 3-morpholinopropionate, methoxycarbonylmethyl 3-piperidinopropionate, 2-hydroxyethyl 3-(1-pyrrolidinyl)propionate, 2-acetoxyethyl 3-morpholino-propionate, 2-oxotetrahydrofuran-3-yl 3-(1-pyrrolidinyl)propionate, tetrahydrofurfuryl 3-morpholinopropionate, glycidyl 3-piperidinopropionate, 2-methoxyethyl 3-morpholinopropionate, 2-(2-methoxyethoxy)ethyl 3-(1-pyrrolidinyl)propionate, butyl 3-morpholinopropionate, cyclohexyl 3-piperidinopropionate, α-(1-pyrrolidinyl)methyl-γ-butyrolactone, β-piperidino-γ-butyrolactone, β-morpholino-δ-valerolactone, methyl 1-pyrrolidinylacetate, methyl piperidinoacetate, methyl morpholinoacetate, methyl thiomorpholinoacetate, ethyl 1-pyrrolidinylacetate, and 2-methoxyethyl morpholinoacetate.

Also, one or more of cyano-bearing basic compounds having the following general formulae (B3) to (B6) may be blended.

Herein, X, R³⁰⁷ and n are as defined above, and R³⁰⁸ and R³⁰⁹ each are independently a straight or branched alkylene group of 1 to 4 carbon atoms.

Illustrative examples of the cyano-bearing basic compounds having formulae (B3) to (B6) include 3-(diethylamino)propiononitrile, N,N-bis(2-hydroxyethyl)-3-aminopropiononitrile, N,N-bis(2-acetoxyethyl)-3-aminopropiononitrile, N,N-bis(2-formyloxyethyl)-3-aminopropiononitrile, N,N-bis(2-methoxyethyl)-3-aminopropiononitrile, N,N-bis[2-(methoxymethoxy)ethyl]-3-aminopropiononitrile, methyl N-(2-cyanoethyl)-N-(2-methoxyethyl)-3-aminopropionate, methyl N-(2-cyanoethyl)-N-(2-hydroxyethyl)-3-aminopropionate, methyl N-(2-acetoxyethyl)-N-(2-cyanoethyl)-3-aminopropionate, N-(2-cyanoethyl)-N-ethyl-3-aminopropiononitrile, N-(2-cyanoethyl)-N-(2-hydroxyethyl)-3-aminopropiononitrile, N-(2-acetoxyethyl)-N-(2-cyanoethyl)-3-aminopropiononitrile, N-(2-cyanoethyl)-N-(2-formyloxyethyl)-3-aminopropiononitrile, N-(2-cyanoethyl)-N-(2-methoxyethyl)-3-aminopropiononitrile, N-(2-cyanoethyl)-N-[2-(methoxymethoxy)ethyl]-3-amino-propiononitrile, N-(2-cyanoethyl)-N-(3-hydroxy-1-propyl)-3-aminopropiononitrile, N-(3-acetoxy-1-propyl)-N-(2-cyanoethyl)-3-aminopropiononitrile, N-(2-cyanoethyl)-N-(3-formyloxy-1-propyl)-3-aminopropiononitrile, N-(2-cyanoethyl)-N-tetrahydrofurfuryl-3-aminopropiononitrile, N,N-bis(2-cyanoethyl)-3-aminopropiononitrile, diethylaminoacetonitrile, N,N-bis(2-hydroxyethyl)aminoacetonitrile, N,N-bis(2-acetoxyethyl)aminoacetonitrile, N,N-bis(2-formyloxyethyl)aminoacetonitrile, N,N-bis(2-methoxyethyl)aminoacetonitrile, N,N-bis[2-(methoxymethoxy)ethyl]amino-acetonitrile, methyl N-cyanomethyl-N-(2-methoxyethyl)-3-aminopropionate, methyl N-cyanomethyl-N-(2-hydroxyethyl)-3-aminopropionate, methyl N-(2-acetoxyethyl)-N-cyanomethyl-3-aminopropionate, N-cyanomethyl-N-(2-hydroxyethyl)aminoacetonitrile, N-(2-acetoxyethyl)-N-(cyanomethyl)aminoacetonitrile, N-cyanomethyl-N-(2-formyloxyethyl)aminoacetonitrile, N-cyanomethyl-N-(2-methoxyethyl)aminoacetonitrile, N-cyanomethyl-N-[2-(methoxymethoxy)ethyl)aminoacetonitrile, N-cyanomethyl-N-(3-hydroxy-1-propyl)aminoacetonitrile, N-(3-acetoxy-1-propyl)-N-(cyanomethyl)aminoacetonitrile, N-cyanomethyl-N-(3-formyloxy-1-propyl)aminoacetonitrile, N,N-bis(cyanomethyl)aminoacetonitrile, 1-pyrrolidinepropiononitrile, 1-piperidinepropiononitrile, 4-morpholine-propiononitrile, 1-pyrrolidineacetonitrile, 1-piperidine-acetonitrile, 4-morpholineacetonitrile, cyanomethyl 3-diethylaminopropionate, cyanomethyl N,N-bis(2-hydroxyethyl)-3-aminopropionate, cyanomethyl N,N-bis(2-acetoxyethyl)-3-aminopropionate, cyanomethyl N,N-bis(2-formyloxyethyl)-3-aminopropionate, cyanomethyl N,N-bis(2-methoxyethyl)-3-aminopropionate, cyanomethyl N,N-bis[2-(methoxymethoxy)ethyl]-3-aminopropionate, 2-cyanoethyl 3-diethylaminopropionate, 2-cyanoethyl N,N-bis(2-hydroxyethyl)-3-aminopropionate, 2-cyanoethyl N,N-bis(2-acetoxyethyl)-3-aminopropionate, 2-cyanoethyl N,N-bis(2-formyloxyethyl)-3-aminopropionate, 2-cyanoethyl N,N-bis(2-methoxyethyl)-3-aminopropionate, 2-cyanoethyl N,N-bis[2-(methoxymethoxy)ethyl]-3-aminopropionate, cyanomethyl 1-pyrrolidine-propionate, cyanomethyl 1-piperidinepropionate, cyanomethyl 4-morpholinepropionate, 2-cyanoethyl 1-pyrrolidinepropionate, 2-cyanoethyl 1-piperidinepropionate, and 2-cyanoethyl 4-morpholinepropionate.

The basic compound is preferably formulated in an amount of 0.001 to 10 parts, and especially 0.01 to 1 part, per part of the photoacid generator. Less than 0.001 part of the basic compound may fail to achieve the desired effects thereof, while the use of more than 10 parts would result in too low a sensitivity and resolution.

Other Components

In the resist composition, a compound bearing a ≡C—COOH group in a molecule may be blended. Exemplary, non-limiting compounds bearing a ≡C—COOH group include one or more compounds selected from Groups I and II below. Including this compound improves the PED stability of the resist and ameliorates edge roughness on nitride film substrates.

Group I:

Compounds in which some or all of the hydrogen atoms on the phenolic hydroxyl groups of the compounds of general formulas (A1) to (A10) below have been replaced with —R⁴⁰¹—COOH (wherein R⁴⁰¹ is a straight or branched alkylene of 1 to 10 carbon atoms), and in which the molar ratio C/(C+D) of phenolic hydroxyl groups (C) to ≡C—COOH groups (D) in the molecule is from 0.1 to 1.0.

In these formulas, R⁴⁰⁸ is hydrogen or methyl; R⁴⁰² and R⁴⁰³ are each hydrogen or a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms; R⁴⁰⁴ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or a —(R⁴⁰⁹)_(h)—COOR′ group (R′ being hydrogen or —R⁴⁰⁹—COOH); R⁴⁰⁵ is —(CH₂)₂— (wherein i is 2 to 10), an arylene of 6 to 10 carbon atoms, carbonyl, sulfonyl, an oxygen atom, or a sulfur atom; R⁴⁰⁶ is an alkylene of 1 to 10 carbon atoms, an arylene of 6 to 10 carbon atoms, carbonyl, sulfonyl, an oxygen atom, or a sulfur atom; R⁴⁰⁷ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or a hydroxyl-substituted phenyl or naphthyl; R⁴⁰⁹ is a straight or branched alkylene of 1 to 10 carbon atoms; R⁴¹⁰ is hydrogen, a straight or branched alkyl or alkenyl of 1 to 8 carbon atoms, or a —R⁴¹¹—COOH group; R⁴¹¹ is a straight or branched alkylene of 1 to 10 carbon atoms; the letter j is an integer from 0 to 5; u and h are each 0 or 1; s1, t1, s2, t2, s3, t3, s4, and t4 are each numbers which satisfy s1+t1=8, s2+t2=5, s3+t3=4, and s4+t4=6, and are such that each phenyl skeleton has at least one hydroxyl group; κ is a number such that the compound of formula (A6) may have a weight average molecular weight of 1,000 to 5,000; and λ is a number such that the compound of formula (A7) may have a weight average molecular weight of 1,000 to 10,000.

Group II:

Compounds of general formulas (A11) to (A15) below.

In these formulas, R⁴⁰², R⁴⁰³, and R⁴¹¹ are as defined above; R⁴¹² is hydrogen or hydroxyl; s5 and t5 are numbers which satisfy s5≧0, t5≧0, and s5+t5=5; and h′ is equal to 0 or 1.

Illustrative, non-limiting examples of the compound bearing a ≡C—COOH group include compounds of the general formulas AI-1 to AI-14 and AII-1 to AII-10 below.

In the above formulas, R″ is hydrogen or a CH₂COOH group such that the CH₂COOH group accounts for 10 to 100 mol % of R″ in each compound, α and κ are as defined above.

The compound bearing a ≡C—COOH group within the molecule may be used singly or as combinations of two or more thereof.

The compound bearing a ≡C—COOH group within the molecule is added in an amount ranging from 0 to 5 parts, preferably 0.1 to 5 parts, more preferably 0.1 to 3 parts, further preferably 0.1 to 2 parts, per 100 parts of the base resin. More than 5 parts of the compound can reduce the resolution of the resist composition.

The resist composition of the invention may additionally include an acetylene alcohol derivative for the purpose of enhancing the shelf stability. Preferred acetylene alcohol derivatives are those having the general formula (S1) or (S2) below.

In the formulas, R⁵⁰¹, R⁵⁰², R⁵⁰³, R⁵⁰⁴, and R⁵⁰⁵ are each hydrogen or a straight, branched, or cyclic alkyl of 1 to 8 carbon atoms; and X and Y are each 0 or a positive number, satisfying 0≦X≦30, 0≦Y≦30, and 0≦X+Y≦40.

Preferable examples of the acetylene alcohol derivative include Surfynol 61, Surfynol 82, Surfynol 104, Surfynol 104E, Surfynol 104H, Surfynol 104A, Surfynol TG, Surfynol PC, Surfynol 440, Surfynol 465, and Surfynol 485 from Air Products and Chemicals Inc., and Surfynol E1004 from Nisshin Chemical Industry K.K.

The acetylene alcohol derivative is preferably added in an amount of 0.01 to 2% by weight, and more preferably 0.02 to 1% by weight, per 100% by weight of the resist composition. Less than 0.01% by weight would be ineffective for improving coating characteristics and shelf stability, whereas more than 2% by weight would result in a resist having a low resolution.

The resist composition of the invention may include optional ingredients, for example, a surfactant which is commonly used for improving the coating characteristics. Optional ingredients may be added in conventional amounts so long as this does not compromise the objects of the invention.

Nonionic surfactants are preferred, examples of which include perfluoroalkylpolyoxyethylene ethanols, fluorinated alkyl esters, perfluoroalkylamine oxides, perfluoroalkyl EO-addition products, and fluorinated organosiloxane compounds. Useful surfactants are commercially available under the trade names Florade FC-430 and FC-431 from Sumitomo 3M, Ltd., Surflon S-141, S-145, KH-10, KH-20, KH-30 and KH-40 from Asahi Glass Co., Ltd., Unidyne DS-401, DS-403 and DS-451 from Daikin Industry Co., Ltd., Megaface F-8151 from Dai-Nippon Ink & Chemicals, Inc., and X-70-092 and X-70-093 from Shin-Etsu Chemical Co., Ltd. Preferred surfactants are Florade FC-430 from Sumitomo 3M, Ltd., KH-20 and KH-30 from Asahi Glass Co., Ltd., and X-70-093 from Shin-Etsu Chemical Co., Ltd.

Pattern formation using the resist composition of the invention may be carried out by a known lithographic technique. For example, the resist composition is applied onto a substrate such as a silicon wafer by spin coating or the like to form a resist film having a thickness of 0.2 to 2.0 μm, which is then pre-baked on a hot plate at 60 to 150° C. for 1 to 10 minutes, and preferably at 80 to 130° C. for 1 to 5 minutes. A patterning mask having the desired pattern is then placed over the resist film, and the film exposed through the mask to an electron beam or to high-energy radiation such as deep-UV rays, an excimer laser, or x-rays in a dose of about 1 to 200 mJ/cm², and preferably about 5 to 100 mJ/cm², then post-exposure baked (PEB) on a hot plate at 60 to 150° C. for 1 to 5 minutes, and preferably at 80 to 130° C. for 1 to 3 minutes. Finally, development is carried out using as the developer an aqueous alkali solution, such as a 0.1 to 5% (preferably 2 to 3%) aqueous solution of tetramethylammonium hydroxide (TMAH), this being done by a conventional method such as dipping, puddling, or spraying for a period of 0.1 to 3 minutes, and preferably 0.5 to 2 minutes. These steps result in the formation of the desired pattern on the substrate. Of the various types of high-energy radiation that may be used, the resist composition of the invention is best suited to fine pattern formation with, in particular, deep-UV rays having a wavelength of 248 to 193 nm, an excimer laser, x-rays, or an electron beam. The desired pattern may not be obtainable outside the upper and lower limits of the above range.

The resist composition comprising the inventive polymer as a base resin lends itself to micropatterning with electron beams or deep-UV rays since it is sensitive to high-energy radiation and has excellent sensitivity, resolution, and etching resistance. Especially because of the minimized absorption at the exposure wavelength of an ArF or KrF excimer laser, a finely defined pattern having sidewalls perpendicular to the substrate can easily be formed.

EXAMPLE

Synthesis Examples and Examples are given below by way of illustration and not by way of limitation. The abbreviation Mw is a weight average molecular weight as measured by GPC using a polystyrene standard, and SEM is scanning electron microscope.

Polymers within the scope of the invention were synthesized by the following procedure.

Synthesis Example 1

Synthesis of Polymer 1

A mixture of 70.2 g of 2-methyl-2-adamantyl methacrylate, 62.4 g of 2-ethylbicyclo[2.2.1]heptan-2-yl methacrylate (the ester bond is located on the exo-side relative to the bicyclo[2.2.1]heptane ring), 112.0 g of 5-methoxycarbonyl-3-oxo-2-oxatricyclo[4.2.1.0^(4,8)]nonan-9-yl methacrylate, 1.40 g of 2-mercaptoethanol, and 611.5 g of tetrahydrofuran was heated at 60° C. To the solution was added 3.28 g of 2,2′-azobisisobutyronitrile. The solution was stirred for 15 hours while keeping at 60° C. The reaction solution was cooled to room temperature and dissolved in 500 ml of acetone, which with vigorous stirring, was added dropwise to 10 liters of isopropyl alcohol. The resulting solids were collected by filtration and dried in vacuum at 40° C. for 15 hours, obtaining a polymer in white powder solid form. The amount was 217.2 g and the yield was 88.8%. This is designated Polymer 1.

Synthesis Examples 2-8

Synthesis of Polymers 2-8

Polymers 2 to 8 were synthesized by the same procedure as above or a well-known procedure.

Resist compositions were formulated using inventive polymers as the base resin and examined for resolution.

Examples 1-20 & Comparative Examples 1-8

Resist compositions were prepared by using Polymers 1 to 8 or comparative Polymers 9 to 12, shown below, as the base resin, and dissolving the polymer, a photoacid generator, and a basic compound in a solvent in accordance with the formulation shown in Tables 1 and 2. These compositions were each filtered through a polytetrafluoro-ethylene filter (pore diameter 0.2 μm), thereby giving resist solutions.

These resist solutions were spin coated onto silicon wafers having an antireflection film (ARC25 by Nissan Chemical Co., Ltd., 77 nm thick) coated thereon, then heat treated at 130° C. for 60 seconds to give resist films having a thickness of 375 nm. The resist films were exposed using an ArF excimer laser stepper (Nikon Corporation; NA 0.55), then heat treated at 100° C. to 140° C. for 60 seconds, and puddle developed with a solution of 2.38% tetramethyl-ammonium hydroxide in water for 60 seconds, thereby giving 1:1 line-and-space patterns.

The wafers as developed were sectioned and observed under sectional SEM. The optimal dose (Eop, mJ/cm²) was defined as the exposure dose which provided a 1:1 resolution at the top and bottom of a 0.20 μm line-and-space pattern. The resolution of the resist under evaluation was defined as the minimum line width (μm) of the lines and spaces that separated at the optimal dose. The shape of the resist pattern was examined under a SEM and classified into rectangular, rounded head, T-top, forward taper or reverse taper. By observing whether or not side walls were serrated, the resist film was rated “O” for smoothness or “X” for serration.

The composition and test results of the resist materials are shown in Tables 1 and 2. The photoacid generator, basic compound and solvents used are as follows. It is noted that the solvents contained 0.01% by weight of surfactant KH-20 (Asahi Glass Co., Ltd.).

TPSNf: triphenylsulfonium nonafluorobutanesulfonate

TPSTf: triphenylsulfonium trifluoromethanesulfonate

TMMEA: trismethoxymethoxyethylamine

TAEA: trisacetoxyethylamine

PGMEA: propylene glycol methyl ether acetate

CyHO: cyclohexanone

TABLE 1 Photoacid Basic PEB Resin generator compound Solvent temp., Eop, Resolution, Sidewall Example (pbw) (pbw) (pbw) (pbw) ° C. mJ/cm² μm Shape serration 1 Polymer 1 TPSNf TMMEA PGMEA 110 28.0 0.15 rectangular ◯ (80) (1.090) (0.236) (480) 2 Polymer 2 TPSNf TMMEA PGMEA 110 27.0 0.15 rectangular ◯ (80) (1.090) (0.236) (480) 3 Polymer 3 TPSNf TMMEA PGMEA 110 27.0 0.15 rectangular ◯ (80) (1.090) (0.236) (480) 4 Polymer 4 TPSNf TMMEA PGMEA 110 25.0 0.16 rectangular ◯ (80) (1.090) (0.236) (480) 5 Polymer 5 TPSNf TMMEA PGMEA 110 28.0 0.15 rectangular ◯ (80) (1.090) (0.236) (480) 6 Polymer 6 TPSNf TMMEA PGMEA 110 26.0 0.15 rectangular ◯ (80) (1.090) (0.236) (480) 7 Polymer 7 TPSNf TMMEA PGMEA 110 28.0 0.15 rectangular ◯ (80) (1.090) (0.236) (480) 8 Polymer 8 TPSNf TMMEA PGMEA 110 30.0 0.15 rectangular ◯ (80) (1.090) (0.236) (480) 9 Polymer 3 TPSTf TMMEA PGMEA 110 25.0 0.16 rectangular ◯ (80) (0.800) (0.236) (480) 10 Polymer 5 TPSTf TMMEA PGMEA 110 26.0 0.15 rectangular ◯ (80) (0.800) (0.236) (480) 11 Polymer 1 TPSNf TMMEA PGMEA 110 26.0 0.15 rectangular ◯ (40) (1.090) (0.236) (480) Polymer 4 (40) 12 Polymer 1 TPSNf TMMEA PGMEA 110 29.0 0.16 rectangular ◯ (40) (1.090) (0.236) (480) Polymer 9 (40) 13 Polymer 1 TPSNf TMMEA PGMEA 110 24.0 0.16 rectangular ◯ (80) (1.090) (0.472) (480) TPSTf (0.800) 14 Polymer 1 TPSNf TAEA PGMEA 110 25.0 0.15 rectangular ◯ (80) (1.090) (0.462) (480) TPSTf (0.800) 15 Polymer 1 TPSNf TAEA PGMEA 110 26.0 0.15 rectangular ◯ (80) (2.180) (0.462) (480) 16 Polymer 3 TPSNf TAEA PGMEA 110 26.0 0.15 rectangular ◯ (80) (2.180) (0.462) (480) 17 Polymer 5 TPSNf TAEA PGMEA 110 26.0 0.15 rectangular ◯ (80) (2.180) (0.462) (480) 18 Polymer 6 TPSNf TAEA PGMEA 100 25.0 0.15 rectangular ◯ (80) (2.180) (0.462) (480) 19 Polymer 6 TPSNf TAEA PGMEA 110 25.0 0.15 rectangular ◯ (80) (2.180) (0.462) (480) 20 Polymer 6 TPSNf TAEA PGMEA 120 24.0 0.15 rectangular ◯ (80) (2.180) (0.462) (480)

TABLE 2 Photoacid Basic PEB Comparative Resin generator compound Solvent temp., Eop, Resolution, Sidewall Example (pbw) (pbw) (pbw) (pbw) ° C. mJ/cm² μm Shape serration 1 Polymer 9 TPSNf TMMEA CyHO 130 28.0 0.16 rectangular X (80) (1.090) (0.236) (560) 2 Polymer 10 TPSNf TMMEA CyHO 130 32.0 0.17 T-top X (80) (1.090) (0.236) (560) 3 Polymer 11 TPSNf TMMEA CyHO 130 34.0 0.17 T-top X (80) (1.090) (0.236) (560) 4 Polymer 12 TPSNf TMMEA CyHO 110 30.0 0.16 rectangular X (80) (1.090) (0.236) (560) 5 Polymer 9 TPSNf TAEA CyHO 130 26.0 0.17 forward ◯ (80) (2.180) (0.462) (560) taper 6 Polymer 10 TPSNf TAEA CyHO 120 36.0 0.16 forward X (80) (2.180) (0.462) (560) taper 7 Polymer 10 TPSNf TAEA CyHO 130 31.0 0.16 forward X (80) (2.180) (0.462) (560) taper 8 Polymer 10 TPSNf TAEA CyHO 140 29.0 0.16 forward ◯ (80) (2.180) (0.462) (560) taper

It is seen from Tables 1 and 2 that the resist compositions within the scope of the invention have a high sensitivity and resolution upon ArF excimer laser exposure, free from sidewall serration and allow for a wide margin he heat treatment temperature.

Japanese Patent Application No. 2001-277156 is incorporated herein by reference.

Although some preferred embodiments have been described, many modifications and variations may be made thereto in light of the above teachings. It is therefore to be understood that the invention may be practiced otherwise than as specifically described without departing from the scope of the appended claims. 

What is claimed is:
 1. A polymer comprising recurring units of the general formula (1) and recurring units of the general formula (2) and having a weight average molecular weight of 1,000 to 500,000,

wherein R¹ and R³ each are hydrogen or methyl, R² and R⁴ each are a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, R⁵, R⁶, R⁷ and R⁸ each are hydrogen, or a pair of R⁵ and R⁷ and a pair of R⁶ and R⁸ each stand for a group of atoms to form trimethylene or 1,3-cyclopentylene.
 2. The polymer of claim 1 further comprising recurring units of the general formula (3):

wherein R⁹ is hydrogen or methyl, R¹⁰ is hydrogen or a straight, branched or cyclic alkyl group of 1 to 15 carbon atoms, R¹¹ is hydrogen or CO₂R¹², R¹² is a straight, branched or cyclic alkyl group having 1 to 15 carbon atoms in which at least one oxygen atom may intervene in any carbon-to-carbon bond, and X is methylene or an oxygen atom.
 3. A resist composition comprising the polymer of claim 1 as a base resin.
 4. A process for forming a resist pattern comprising the steps of: applying the resist composition of claim 3 onto a substrate to form a coating, heat treating the coating and then exposing it to high-energy radiation or electron beam through a photo mask, and optionally heat treating the exposed coating and developing it with a developer. 